Material frequently used in manufacturing jacketed gaskets and Ring Joints. Due to its low resistance to corrosion it should not be used in water, diluted acids or saline solutions. It may be used in some alkalis and in some concentrated acids. Temperature limit 900° F (500° C).

Approximate Hardness: 90 to 120 HB.

Alloy with 18% Cr and 8% Ni is the material most used in the manufacturing of industrial gaskets due to its excellent resistance to corrosion, low cost and availability in the market. Its maximum operating temperature is 1400° F (760° C). Due to Stress and Intergranular Corrosion, its continuous service temperature is limited to 790° F (420° C).

Approximate Hardness: 160 HB.

It has the same resistance to corrosion as the AISI 304. Since its Carbon content is limited to 0.03%, it has less Intergranular Carbon precipitation and therefore less Intergranular Corrosion. Its operational limit for continuous service is 1400° F (760° C). It is susceptible to Stress Corrosion.

Approximate Hardness: 160 HB and in some cases,140 HB.

This alloy with 18% Ni, 13% Cr and 2% Mo, offers excellent resistance to corrosion. It can have carbonate precipitation at temperatures between 860° F (460° C) and 1650° F (900° C), under severe corrosion conditions. Maximum recommended temperature for continuous service is 1400° F (760° C).

Approximate Hardness: 160 HB.

It has the same chemical composition as the AISI 316 but its Carbon content is limited to 0.03%, which inhibits the Intergranular Carbon precipitation and consequently, the Intergranular Corrosion. The maximum service temperature is 1400° F (760° C).

Approximate Hardness: 160 HB.

Austenitic stainless steel alloy with 18% Cr and 10% Ni stabilized with Ti, which reduces the Intergranular Carbon precipitation and also the Intergranular Corrosion. It can be used in temperatures up to 1500°F (815°C).

Approximate Hardness: 160 HB.

Alloy similar to the AISI 304 stabilized with Cb and Ta to reduce carbonate precipitation and Intergranular Corrosion. It is subject to Stress Corrosion. Has good performance in high temperature corrosive service. Maximum temperature: 1550° F (815° C).

Approximate Hardness: 160 HB.

Alloy with 99% Ni, offers great resistance to caustic solutions, even thought it does not have the same global resistance of Monel. It is also used in spiral wound and jacketed gaskets for special applications. Maximum operating temperature: 1400 F (760° C).

Approximate Hardness: 110 HB.

Material often used in small dimension gaskets, where the maximum seating stress is limited. Maximum operating temperature: 500° F (260° C).

Approximate Hardness: 80 HB.

Due to its excellent resistance to corrosion and easy handling it is very often used in manufacturing gaskets. Maximum service temperature: 860° F (460° C).

Approximate Hardness: 35 HB.

Alloy with 77% Ni, 15% Cr and 7% Fe, it has excellent corrosion resistance from cryogenic to high temperatures. Temperature limit: 2000° F (1100° C).

Approximate Hardness: 150 HB.

Metal with excellent corrosion properties in elevated temperatures, oxidant service, Nitric acid and caustic solutions. Temperature limit: 2000° F (1100° C).

Approximate Hardness: 215 HB.

Alloy with 99% Ni, offers great resistance to caustic solutions, even thought it does not have the same global resistance of Monel. It is also used in spiral wound and jacketed gaskets for special applications. Maximum operating temperature: 1400 F (760° C).

Approximate Hardness: 110 HB.